AÇO DUPLEX LDX 2101 SUBMETIDO À NITRETAÇÃO POR IMPLANTAÇÃO IÔNICA, IMPLANTAÇÃO IÔNICA POR IMERSÃO EM PLASMA E DESCARGA LUMINOSA: PROPRIEDADES MECÂNICAS E TRIBOLÓGICAS

Abstract

In the present work showing the results on mechanical and tribological properties of duplex stainless steel LDX2101 nitriding by Ion Implantation (II), Plasma Immersion Ion Implantation (PI3) and Glow Discharge (GD). Nitrogen ion implantation was performed at room temperature and 350 C. The nitrogen fluencies were combined to obtain an atomic nitrogen concentration of 27 %. The PI3 was carried out with temperatures of 300 and 350 C working in N2 atmosphere during 3 hours. For GD, the working conditions were gas mixture N2/H2 (in the ratio 80%/20%, 60%/40% and 20%/80%) and N2/CH4 (in the ratio 98%/02%) during 3 hours at temperatures of 300, 350 and 380 C. Structural characterizations of the modified layers were performed by X-Ray Diffraction (XRD) with Bragg-Brentano geometry. Hardness was obtained by instrumented indentation using Oliver and Pharr method’s with Berkovich indenter. Tribological tests were evaluated by reciprocating sliding with a WC(Co) sphere (counter body). XRD patterns for II samples showing only the formation of γN, however, samples treated by GD and PI3 showed the formation of γ’Fe4N and Fe2+XN, over there γN, as a function of the working temperature and nitriding atmosphere. After the nitriding hardness values between 8 and 20 GPa in comparison to 3 GPa of the bulk was obtained. The hardness profile of samples treated by GD at 350 and 380 C exhibit plateaulike for values of hardness between 13 and 20 GPa, indicate the formation of a thicker nitrited layer. The friction coefficient for II samples showed a strong adhesive wear. PI3 samples exhibit long running-in regimes compared to II and untreated samples. GD samples showing a predominant abrasive wear because ploughing of surface for asperities and wear particles formed between the surface and counter body. The significant decrease in the wear was observed in all GD samples, with a reduction of one order of magnitude compared to untreated sample.