metadata.dc.type: Dissertação
Title: Estudo do processamento de polietileno de ultra-alta massa molar(Peuamm)e polietileno glico (PEG) por moagem de alta energia
metadata.dc.creator: Gabriel, Melina Correa
metadata.dc.contributor.advisor1: Cintho, Osvaldo Mitsuyuki
metadata.dc.contributor.referee1: Scuracchio, Carlos Henrique
metadata.dc.contributor.referee2: Carvalho, Benjamim de Melo
metadata.dc.description.resumo: Este trabalho exploratório teve por objetivo estudar as modificações promovidas por moagem de alta energia no de polietileno de ultra-alta massa molar (PEUAMM) e sua mistura com polietileno glicol (PEG), que podem ser de interesse para auxiliar um posterior processamento do PEUAMM. As moagens foram realizadas em um moinho do tipo attritor, um tipo de moinho que pode ser usado tanto em laboratório quanto em escala industrial. Foram variadas as velocidades de rotação na moagem do PEUAMM, além das concentrações de PEG, quando feita a mistura. As amostras foram caracterizadas por microscopia eletrônica de varredura (MEV), microscopia de força atômica (MFA), calorimetria exploratória diferencial (DSC) e difração de raios X. A moagem de alta energia do material modificou a forma das partículas de PEUAMM, passando de arredondadas a flakes, com a evolução do processo de moagem, fazendo com que a densidade aparente do polímero diminuísse muito comparado ao polímero não moído. A moagem também proporcionou mudança estrutural, permitindo a formação de fase monoclínica em detrimento da ortorrômbica. A medida que se aumentou a rotação do moinho até 500 rpm, houve um crescimento da fase monoclínica. Apenas para 600 rpm, a quantidade dessa fase sofreu decréscimo, devido possivelmente ao aumento da frequência de choques e da temperatura de processamento, fazendo com que a estrutura monoclínica retornasse à estrutura ortorrômbica original. Na mistura de PEUAMM com PEG, a moagem provavelmente permitiu redução das partículas e a melhor dispersão de PEG na matriz de PEUAMM. Também se observaram mudanças nas características térmicas dos polímeros na mistura após moagem. Ocorreu mudança na cinética de crescimento dos cristais de PEUAMM e mudança no comportamento de cristalização do PEG, comportamento este que não ocorreu para o PEUAMM moído ou para a mistura de PEUAMM com PEG antes da moagem. Possivelmente, as partículas dispersas de PEG atuaram como barreiras ao crescimento da fase cristalina do PEUAMM e houve diminuição da temperatura de cristalização do PEG, na mistura com PEUAMM após moagem.
Abstract: The intention of this exploratory research is to study the modifications provided by high-energy mechanical milling in ultra-high molecular weight polyethylene (UHMWPE) and mixtures of this polymer with polyethylene glycol (PEG). These modifications can be of interest for future processing of UHMWPE. The mechanical milling was performed in an attritor mill, a type of mill that can be used in laboratory as well as in industry. The millings of UHMWPE were performed in different rotation speeds. For mixtures of UHMWPE and PEG, the amounts of PEG were also different. The samples were characterized by scanning electron microscopy (SEM), atomic force microscopy (AFM), differential scanning calorimetry (DSC) and X-ray diffraction (XRD). The mechanical milling modified the UHMWPE particles morphology: with milling, the almost rounded shape became flat-like shape. This caused the reduction of apparent density of polymer after milling. The mechanical milling also provided structural changes. With the increasing of the rotation speed,there was the increasing of the monoclinic phase and the decreasing of the orthorhombic, up to 500 rpm. For 600 rpm, the amount of monoclinic phase decreased. In this rotation, the deformation rate probably increased the process temperature, allowing the monoclinic phase to return to its initial structural orthorhombic form. In mixtures of UHMWPE and PEG, after mechanical milling, the particles of PEG were probably reduced and better dispersed in the UHMWPE matrix. Changes in thermal characteristics of polymers also could be noted. The kinetics of UHMWPE crystal growth changed, as well as the behavior of PEG crystallization. Feasibly, dispersed particles of PEG acted as physical barriers against the crystalline phase growth of UHMWPE and the crystallization temperature of PEG decreased, when the UHMWPE and PEG mixtures were milled.
Keywords: Polietileno de ultra-alta massa molar (PEUAMM)
Moagem de alta energia
Moinho attritor
Deconvolução
Polietileno glicol (PEG)
Ultra-high molecular weight polyethylene (UHMWPE)
High-energy mechanical milling
Attritor mill
Deconvolution
Polyethylene glycol (PEG)
metadata.dc.subject.cnpq: CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA
metadata.dc.language: por
metadata.dc.publisher.country: BR
Publisher: UNIVERSIDADE ESTADUAL DE PONTA GROSSA
metadata.dc.publisher.initials: UEPG
metadata.dc.publisher.department: Desenvolvimento e Caracterização de Materiais
metadata.dc.publisher.program: Programa de Pós-Graduação em Engenharia e Ciências de Materiais
Citation: GABRIEL, Melina Correa. Estudo do processamento de polietileno de ultra-alta massa molar(Peuamm)e polietileno glico (PEG) por moagem de alta energia. 2010. 80 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2010.
metadata.dc.rights: Acesso Aberto
URI: http://tede2.uepg.br/jspui/handle/prefix/1395
Issue Date: 29-Mar-2010
Appears in Collections:Programa de Pós - Graduação em Engenharia e Ciências de Materiais

Files in This Item:
File SizeFormat 
Melina Correa Gabriel.pdf5.78 MBAdobe PDFView/Open


Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.