Title: | SÍNTESE DE MATERIAL PARTICULADO AMARELO A BASE DE TiO2 CONTENDO MoO3 E Bi2O3 |
metadata.dc.creator: | Silva, Renata Martins da |
metadata.dc.contributor.advisor1: | Tebcherani, Sérgio Mazurek |
metadata.dc.contributor.advisor-co1: | Kubaski, Evaldo Toniolo |
metadata.dc.contributor.referee1: | Moreira, Mário Lúcio |
metadata.dc.contributor.referee2: | Zara, Alfredo José |
metadata.dc.description.resumo: | Foi sintetizado um material particulado a base de TiO2, contendo uma pequena quantidade de compostos de bismuto e de molibdênio apresentando boa reprodutibilidade. O material foi produzido a partir de uma composição de 99% (mol%) de rutilo TiO2 e 1% de MoO3, previamente misturados e calcinado a 1200 °C. A composição estudada consistia de 99,8% da mistura acima e 0,2% de subnitrato de bismuto hexahidratado, Bi5O(OH)9 (NO3)4.6H2O. Esta mistura em pó [(99,8% de TiO2 + MoO3 e 0,2% de Bi5O(OH)9 (NO3) 4.6H2O)], foi homogeneizada e calcinada em forno tubular a 1200 ºC, utilizando-se quatro taxas de aquecimento diferentes: 1, 30, 40 e 60 °C /min. O pó calcinado foi caracterizado por difração de raios X (DRX) para identificação das fases resultantes, por microscopia eletrônica de varredura (MEV) para avaliação da microestrutura e grau de aglomeração dos pós, o tamanho de partículas foi estimado por espectroscopia de fotocorrelação (PCS) e as propriedades colorimétricas através das coordenadas CIEL*a*b* . O DRX indicou a presença das fases TiO2, α-Bi2O3, γ-Bi2MoO6, Bi2Ti2O7, Bi2Ti4O11 sendo estas dependentes das taxas de aquecimento utilizadas. A cor amarela foi atribuída à presença de α-Bi2O3, -Bi2MoO6 e Bi2Ti2O7. As taxas de aquecimento diferentes não apresentaram nenhuma influência relevante sobre a morfologia do pó, porém o tamanho de partícula do pó mostrou-se adequado para a utilização do material, como um pigmento inorgânico. |
Abstract: | Was synthesized particulate material based on containing a small amount of bismuth compounds and molybdenum with satisfactory reproducibility. The material was produced starting from a composition of 99% (mol %) of rutile TiO2 and 1% of MoO3, which were previously mixed and calcined at 1200ºC. The composition studied consisted of 99.8% of the above mixture and 0.2% of bismuth subnitrate hexahydrate, Bi5O(OH)9 NO3)4.6H2O. This powder mixture [(99.8% of TiO2+MoO3 and 0.2% of Bi5O(OH)9 (NO3)4.6H2O)] was homogenized and calcined in tubular furnace at 1200ºC using four different heating rates: 1, 30, 40 e 60 °C/min. The ascalcined powder was characterized by X-ray diffraction (XRD) for identification of the phases resulting, scanning electron microscopy (SEM) to evaluate the microstructure and degree of gglomeration of powders and particle size was estimated by laser scattering technique. The color properties were expressed as CIEL*a*b* coordinates. X-ray patterns indicated the presence of TiO2, Bi2O3, γ-Bi2MoO6, Bi2Ti2O7, Bi2Ti4O11 depending on the heating rate. The yellow color was attributed to the presence of α-Bi2O3, Bi2MoO6 e Bi2Ti2O7. The different heating rates showed no relevant influence on the powder morphology, but the particle size of the powder was suitable for using the material as an inorganic pigment. |
Keywords: | pigmento inorgânico rutilo TiO2 Bi2O3 Bi2MoO6 Bi2Ti2O7 inorganic pigment rutile TiO2 Bi2O3 Bi2MoO6 Bi2Ti2O7 |
metadata.dc.subject.cnpq: | CNPQ::ENGENHARIAS::ENGENHARIA DE MATERIAIS E METALURGICA |
metadata.dc.language: | por |
metadata.dc.publisher.country: | BR |
Publisher: | UNIVERSIDADE ESTADUAL DE PONTA GROSSA |
metadata.dc.publisher.initials: | UEPG |
metadata.dc.publisher.department: | Desenvolvimento e Caracterização de Materiais |
metadata.dc.publisher.program: | Programa de Pós-Graduação em Engenharia e Ciências de Materiais |
Citation: | SILVA, Renata Martins da. SÍNTESE DE MATERIAL PARTICULADO AMARELO A BASE DE TiO2 CONTENDO MoO3 E Bi2O3. 2013. 46 f. Dissertação (Mestrado em Desenvolvimento e Caracterização de Materiais) - UNIVERSIDADE ESTADUAL DE PONTA GROSSA, Ponta Grossa, 2013. |
metadata.dc.rights: | Acesso Aberto |
URI: | http://tede2.uepg.br/jspui/handle/prefix/1431 |
Issue Date: | 22-Feb-2013 |
Appears in Collections: | Programa de Pós - Graduação em Engenharia e Ciências de Materiais |
Files in This Item:
File | Size | Format | |
---|---|---|---|
Renata Martins Silva.pdf | 2.78 MB | Adobe PDF | View/Open |
Items in DSpace are protected by copyright, with all rights reserved, unless otherwise indicated.